its almost....
-
I'm a beginner welder and can tell you your much better then me Joel. I have been doing a lot of research especially with the Lincoln sp135 which that welder looks to be. So what welder is that?
All I'm saying is that your losing a lot of current with that long extension cord. It may be adequate gauge like parker says but where is it plugged into? I suppose to an outlet? How far away is the outlet from the fuse panel and with what gauge wire?
I can guarantee you if the welder was plugged directly into the fuse panel or to a outlet close by those welds would be better.
-
Joel;211087 wrote:
lol, the manual says it will penetrate 3/16... so its not made for that. If either of you wanna come make better welds, your welcome to.I would if i was there
lol, you do realize that means 3/16" full penetration from one side with no joint preparation...............
Good thing you are going for for 100% melt-through on a 1/4" flange when you are welding a 16 ga. tube to it
.little bit of difference going from production welding where coarse machine parameters are set and you are in charge of electrode manipulation only............. don't get more and more into this, the welds look fine, all i am saying is that the machine was not set 100% properly and it wasn't
-
fanaticrockford;211089 wrote:
I'm a beginner welder and can tell you your much better then me Joel. I have been doing a lot of research especially with the Lincoln sp135 which that welder looks to be. So what welder is that?All I'm saying is that your losing a lot of current with that long extension cord. It may be adequate gauge like parker says but where is it plugged into? I suppose to an outlet? How far away is the outlet from the fuse panel and with what gauge wire?
I can guarantee you if the welder was plugged directly into the fuse panel or to a outlet close by those welds would be better.
good call, never thought about it. Yes its a 135t, if you wanna come take a look at it, you are more than welcome...
-
Joel;211044 wrote:
no, were attempting to penetrate a 1/4 inch flange with a 135 amp welder. why do you ask about flux core? what characteristics make it look like it was made with a flux core welder?Because of the spatter. From my experience....there should never be spatter like that from a MIG unless you have something set wrong or are out of gas, heh.
-
zbrown;211102 wrote:
Good thing you are going for for 100% melt-through on a 1/4" flange when you are welding a 16 ga. tube to itIm not going for full penetration, just getting some color on the other side of the flange. And as I understand from my welding experience, I should be penetrating both workpieces as much as possible... Less penetration, less stength. Especially with 2 metals with such different thicknesses... -
zbrown;211102 wrote:
I would if i was therelol, you do realize that means 3/16" full penetration from one side with no joint preparation...............
Good thing you are going for for 100% melt-through on a 1/4" flange when you are welding a 16 ga. tube to it
.little bit of difference going from production welding where coarse machine parameters are set and you are in charge of electrode manipulation only............. don't get more and more into this, the welds look fine, all i am saying is that the machine was not set 100% properly and it wasn't
FYI, I'm not a production jig welder. I set my own machine and change my settings on a regular basis, out of position, mostly V. down and overhead welding
And as I understand from my welding experience, I should be penetrating both workpieces as much as possible... Less penetration, less stength. Especially with 2 metals with such different thicknesses...
-
All I read into all this was:
Zach is pointing out bad penetration
Joel went to school to learn about penetration and thinks he is fully penetrating properly
Nate doesn't think there should be as much splatter from the said penetrationThen it gets into machines and settings to make perfect penetration....
bunch of homo's
-
Joel;211112 wrote:
And as I understand from my experience, I should be getting penetrated both ass and mouth as much as possible... Less penetration, less fun. Especially with 2 cocks of such different thicknesses...Hmm... I think this was more what he was going for....
-
Hahaha pwnt.
-
FG2;211123 wrote:
All I read into all this was:Zach is pointing out bad penetration
Joel went to school to learn about penetration and thinks he is fully penetrating properly
Nate doesn't think there should be as much splatter from the said penetrationThen it gets into machines and settings to make perfect penetration....
bunch of homo's
grip
Hello! It looks like you're interested in this conversation, but you don't have an account yet.
Getting fed up of having to scroll through the same posts each visit? When you register for an account, you'll always come back to exactly where you were before, and choose to be notified of new replies (either via email, or push notification). You'll also be able to save bookmarks and upvote posts to show your appreciation to other community members.
With your input, this post could be even better 💗
Register Login